- 熔体流动速率 [g/10min]: 65.0
- 密度 [g/cm3]: 0.953
- 拉伸强度 [MPa]: 20.7
- 弯曲强度 [MPa]: 10.3
- 弯曲模量 [MPa]: 1.01
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in³ | |
| Viscosity | 32000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 32000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 46000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 46000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 54000 cP @Shear Rate 300 1/s, Temperature 190 °C | 54000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 65 g/10 min @Load 2.16 kg | 65 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 6.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
| Elongation at Break | 200 % | 200 % | |
| Modulus of Elasticity | 0.669 GPa | 97.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.01 GPa | 146 ksi | |
| Izod Impact Resistance | 3.74 J/cm² | 17.8 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 124 °C | 255 °F | |