- 熔体流动速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.962
- 拉伸强度 [MPa]: 23.0
- 弯曲强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 1.08
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg | 9.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 18.0 MPa | 2610 psi | |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | |
| Elongation at Break | 680 % | 680 % | |
| Modulus of Elasticity | 0.717 GPa | 104 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.08 GPa | 157 ksi | |
| Izod Impact Resistance | 5.90 J/cm² | 28.1 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 129 °C | 264 °F | |