- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.955
- 拉伸强度 [MPa]: 20.7
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | |
| Viscosity | 55000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 55000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 110000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 110000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 180000 cP @Shear Rate 300 1/s, Temperature 190 °C | 180000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 25 g/10 min @Load 2.16 kg | 25 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
| Elongation at Break | 320 % | 320 % | |
| Modulus of Elasticity | 0.607 GPa | 88.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.952 GPa | 138 ksi | |
| Izod Impact Resistance | 4.80 J/cm² | 22.8 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | |