- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 0.956
- 拉伸强度 [MPa]: 23.0
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 1.06
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | |
| Melt Flow | 40 g/10 min @Load 2.16 kg | 40 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | |
| Elongation at Break | 440 % | 440 % | |
| Modulus of Elasticity | 0.696 GPa | 101 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.06 GPa | 154 ksi | |
| Izod Impact Resistance | 2.67 J/cm² | 12.7 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 124 °C | 255 °F | |