- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 2.64 g/m²/day | 0.170 g/100 in²/day | ASTM F1249 |
| Oxygen Transmission Rate | 1488 cc/m²/day | 95.83 cc/100 in²/day | ASTM D3985 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 27.0 MPa | 3920 psi | ASTM D882 |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 890 % | 890 % | ASTM D882 |
| Secant Modulus, MD | 0.840 GPa | 122 ksi | ASTM D882 |
| Secant Modulus, TD | 1.18 GPa | 171 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 0.630 g/micron | 16.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.7 g/micron | 475 g/mil | ASTM D1922 |
| Dart Drop | 1.16 g/micron | 29.5 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 131 °C | 268 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 36 % | 36 % | ASTM D1003 |
| Gloss | 23 % | 23 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |