- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.33 @Frequency 100000 Hz | 2.33 @Frequency 100000 Hz | ASTM D1531 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.17 mm | 508 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | >= 0.00010 @Frequency 100000 Hz | >= 0.00010 @Frequency 100000 Hz | ASTM D1531 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 149 - 177 °C | 300 - 351 °F | Thermoforming surface |
| 227 - 260 °C | 441 - 500 °F | Extrusion | |