- 熔体流动速率 [g/10min]: 51.0
- 密度 [g/cm3]: 0.951
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1.00
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | |
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D792 |
| Melt Flow | 51 g/10 min @Load 2.16 kg, Temperature 190 °C | 51 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 36.0 cm | 14.2 in | NOVA Snake Flow Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50 mm/min; ASTM D638 |
| 29.0 MPa | 4210 psi | 500 mm/min | |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 280 °C | 338 - 536 °F | |