- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.958
- 缺口冲击强度: 7.5
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.48
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | 266 hour | 266 hour | F50, Condition A |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 890 % | 890 % | ASTM D638 |
| Flexural Modulus | 1.48 GPa | 215 ksi | ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | Notched/Unnotched not specified; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |