- 熔体流动速率 [g/10min]: 7.0
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.45
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ISO 1183 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 20 g/10 min @Load 5.00 kg, Temperature 190 °C | 20 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ISO 868/A |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
| Elongation at Break | 400 % | 400 % | ISO 527 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 137 °C | 279 °F | Internal method |
| Vicat Softening Point | 128 °C @Load 1.00 kg | 262 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |