- 熔体流动速率 [g/10min]: 0.6
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.939 g/cc | 0.939 g/cc | ISO 1183 |
| Thickness | 10.0 - 50.0 microns | 0.394 - 1.97 mil | Recommended |
| Melt Flow | 0.60 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.60 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| 15 g/10 min @Load 21.6 kg, Temperature 190 °C | 15 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 % | 550 % | ISO 527-3 |
| Film Elongation at Break, TD | 750 % | 750 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 2.5475 g/micron | 64.706 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 25.475 g/micron | 647.07 g/mil | ISO 6383-2 |
| Dart drop Test | 150 g | 0.331 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 50.0 MPa | 7250 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 400 MPa | 58000 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 500 MPa | 72500 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | Internal method |
| Vicat Softening Point | 119 °C @Load 1.00 kg | 246 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |