- 熔体流动速率 [g/10min]: 30.0
- 拉伸强度 [MPa]: 23.1
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.952 g/cc | 0.952 g/cc | ASTM D792 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 190 °C | 30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 23.1 MPa | 3350 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 120 °C | 248 °F | Rate A (50°C/h), Loading 1 (10 N); ASTM D1525 |