- 熔体流动速率 [g/10min]: 4.8
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.957 g/cc | 0.957 g/cc | ASTM D792 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 122 °C | 252 °F | Rate A (50°C/h), Loading 1 (10 N); ASTM D1525 |