- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.958
- 拉伸强度 [MPa]: 30.3
- 弯曲模量 [MPa]: 1.45
- 热变形温度 [℃]: 81.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50; ASTM D1693 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength, Yield | 30.3 MPa | 4400 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 211 ksi | ASTM D790 |
| Tensile Impact | 74.7 J/cm | 140 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |