- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.956
- 拉伸强度 [MPa]: 29.0
- 热变形温度 [℃]: 75.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Spiral Flow | 33.0 cm | 13.0 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | Crosshead speed - 2"min.; ASTM D638 |
| Elongation at Yield | 7.7 % | 7.7 % | Crosshead speed - 2"min.; ASTM D638 |
| 1% Secant Modulus | 1376 MPa | 199600 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 1.15 GPa | 167 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |