- 熔体流动速率 [g/10min]: 0.057
- 密度 [g/cm3]: 0.959
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.959 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Melt Flow | 0.057 g/10 min | 0.057 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 38.6 MPa | 5600 psi | ASTM D822 |
| Film Tensile Strength at Yield, TD | 33.1 MPa | 4800 psi | ASTM D822 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D822 |
| Film Elongation at Break, TD | 350 % | 350 % | ASTM D822 |
| Dart Drop, Total Energy | 2.44 J | 1.80 ft-lb | ASTM D3420 |
| Elmendorf Tear Strength MD | 10 g | 10 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 34 g | 34 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 84.8 MPa | 12300 psi | ASTM D822 |
| Film Tensile Strength at Break, TD | 64.5 MPa | 9360 psi | ASTM D822 |
| 1% Secant Modulus, MD | 1250 MPa | 181000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 1280 MPa | 186000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | Typical Extrusion |