- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 1.1 g/10 min | 1.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 27.6 MPa | 4000 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 33.1 MPa | 4800 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 0.986 GPa | 143 ksi | ASTM E111 |
| Secant Modulus, TD | 1.38 GPa | 200 ksi | ASTM E111 |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 60.7 MPa | 8800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.8 MPa | 3600 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | |
| Die Opening | 0.1524 cm | 0.06000 in | |
| Blow-up Ratio (BUR) | 2.2 | 2.2 | |