- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.942
- 缺口冲击强度: 0.347
- 弯曲模量 [MPa]: 0.7040
- 热变形温度 [℃]: 59.5
Physical Properties | Metric | English | Comments |
---|---|---|---|
Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in³ | ASTM D1895 |
Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D1505 |
Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Spiral Flow | 43.7 cm | 17.2 in | Equistar test |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 61 | 61 | ASTM D2240 |
Tensile Strength at Break | 21.1 MPa | 3060 psi | 50 mm/min; ASTM D638 |
Elongation at Break | 12 % | 12 % | 50 mm/min; ASTM D638 |
Tensile Modulus | 0.6922 GPa | 100.4 ksi | 1% Secant; 50mm/min; ASTM D638 |
0.9425 GPa | 136.7 ksi | 50mm/min; ASTM D638 | |
Flexural Modulus | 0.7040 GPa | 102.1 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
0.8260 GPa | 119.8 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
0.9411 GPa | 136.5 ksi | 12.5 mm/min; ASTM D790 | |
Izod Impact, Notched | 0.347 J/cm | 0.650 ft-lb/in | ASTM D256 |
NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 | |
Thermal Properties | Metric | English | Comments |
Melting Point | 124.0 °C | 255.2 °F | ASTM D3418 |
Crystallization Temperature | 112.5 °C | 234.5 °F | ASTM D3418 |
Deflection Temperature at 0.46 MPa (66 psi) | 59.5 °C | 139 °F | ASTM D648 |
Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
Processing Properties | Metric | English | Comments |
Rear Barrel Temperature | 232 °C | 450 °F | |
Middle Barrel Temperature | 243 °C | 470 °F | |
Front Barrel Temperature | 246 °C | 475 °F | |
Nozzle Temperature | 246 °C | 475 °F |