- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.951
- 缺口冲击强度: 0.299
- 弯曲模量 [MPa]: 0.9094
- 热变形温度 [℃]: 70.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in³ | ASTM D1895 |
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 35.1 cm | 13.8 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 71 | 71 | ASTM D2240 |
| Tensile Strength at Break | 26.4 MPa | 3830 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 11 % | 11 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.7274 GPa | 105.5 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 0.8839 GPa | 128.2 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 0.9094 GPa | 131.9 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 1.092 GPa | 158.4 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.175 GPa | 170.4 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128.2 °C | 262.8 °F | ASTM D3418 |
| Crystallization Temperature | 114.2 °C | 237.6 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |