- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.948
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 23.4
- 弯曲模量 [MPa]: 0.9653
- 热变形温度 [℃]: 67.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 20 hour | 20 hour | Cond. B, 10%; ASTM D1693 | ||
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 | ||
| Elongation at Break | 1000 % | 1000 % | ASTM D638 | ||
| Flexural Modulus | 0.9653 GPa | 140.0 ksi | 2% Secant; ASTM D790 | ||
| Flexural Modulus, 1% Secant | 1100 MPa | 160000 psi | ASTM D790 | ||
| Izod Impact, Notched | 0.534 J/cm @Temperature -40.0 °C | 1.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 130 °C | 266 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.0 °C | 153 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Gas Fade Resistant | ||||
| Form | Pellet | ||||