- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.560 g/cc | 0.0202 lb/in³ | ASTM D1895 |
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D792 |
| Thickness | 15.0 microns | 0.591 mil | As Tested |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg | 10 g/10 min @Load 47.6 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 380 % @Thickness 0.0150 mm | 380 % @Thickness 0.000591 in | ASTM D882 |
| Film Elongation at Break, TD | 550 % @Thickness 0.0150 mm | 550 % @Thickness 0.000591 in | ASTM D882 |
| Elmendorf Tear Strength, MD | 70.0 g/micron @Thickness 0.0150 mm | 1780 g/mil @Thickness 0.000591 in | ASTM D1922 |
| Elmendorf Tear Strength, TD | 150 g/micron @Thickness 0.0150 mm | 3810 g/mil @Thickness 0.000591 in | ASTM D1922 |
| Dart Drop | 11.3 g/micron @Thickness 0.0150 mm | 287 g/mil @Thickness 0.000591 in | ASTM D1709 A |
| Dart drop Test | 170 g | 0.375 lb | F50; ASTM D1709 A |
| Film Tensile Strength at Break, MD | 60.0 MPa @Thickness 0.0150 mm | 8700 psi @Thickness 0.000591 in | ASTM D882 |
| Film Tensile Strength at Break, TD | 57.0 MPa @Thickness 0.0150 mm | 8270 psi @Thickness 0.000591 in | ASTM D882 |
| 1% Secant Modulus, MD | 1220 MPa @Thickness 0.0150 mm | 177000 psi @Thickness 0.000591 in | ASTM D882 |
| 1% Secant Modulus, TD | 1470 MPa @Thickness 0.0150 mm | 213000 psi @Thickness 0.000591 in | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | Equate Test Method |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 4.0 | 4.0 | 4:1 As Tested |