- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 26.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.18
- 热变形温度 [℃]: 99.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | ASTM D1693 B |
| High Load Melt Index | 10 g/10 min @Load 21.0 kg | 10 g/10 min @Load 46.3 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | >= 750 % | >= 750 % | ASTM D638 |
| Flexural Modulus | 1.18 GPa | 171 ksi | ASTM D790 |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 150 µm/m-°C | 83.3 µin/in-°F | ASTM D969 |
| Melting Point | 135 °C | 275 °F | Equate Test Method |
| Crystallization Temperature | 113 °C | 235 °F | Equate Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 200 °C | 392 °F | |
| Zone 2 | 205 °C | 401 °F | |
| Zone 3 | 205 °C | 401 °F | |
| Zone 4 | 205 °C | 401 °F | |
| Adapter Temperature | 205 °C | 401 °F | |
| Die Temperature | 205 °C | 401 °F | |
| Melt Temperature | 210 °C | 410 °F | |