- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 23.4
- 弯曲模量 [MPa]: 1.03
- 热变形温度 [℃]: 74.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D4883 | ||
| ESCR 100% Igepal® | 10 hour | 10 hour | ASTM D1693 Condition A | ||
| ESCR 10% Igepal® | 8.0 hour | 8.0 hour | ASTM D1693 Condition A | ||
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | 190°C/2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | 2.0 in/min; ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | 2.0 in/min; ASTM D638 | ||
| Flexural Modulus | 1.03 GPa | 150 ksi | 1% Secant; ASTM D790 | ||
| Impact Test | 78.6 J @Thickness 3.17 mm, Temperature -40.0 °C | 58.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 176 J @Thickness 6.35 mm, Temperature -40.0 °C | 130 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 131 °C | 268 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Long Term UV 8 Stabilization | ||||
| Form | Pellet | ||||