- 熔体流动速率 [g/10min]: 0.33
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 26.9
- 弯曲模量 [MPa]: 1.21
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D4883 | ||
| ESCR 100% Igepal® | 70 hour | 70 hour | ASTM D1693 Condition B | ||
| Melt Flow | 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.33 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 | ||
| Elongation at Break | 600 % | 600 % | ASTM D638 | ||
| Flexural Modulus | 1.21 GPa | 175 ksi | Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790 | ||
| Tensile Impact Strength | 189 kJ/m² | 90.0 ft-lb/in² | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 107 °C | 225 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 191 °C | 375 °F | |||
| Descriptive Properties | |||||
| Features | Antistat and Thermal Stabilizer | ||||