- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.942
- 拉伸强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.710
- 热变形温度 [℃]: 54.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D4883 |
Environmental Stress Crack Resistance | 200 hour | 200 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
Elongation at Break | 350 % | 350 % | ASTM D638 |
Flexural Modulus | 0.710 GPa | 103 ksi | ASTM D790 |
Thermal Properties | Metric | English | Comments |
Melting Point | 133 °C | 271 °F | Exxon Method |
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |