- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.942
- 拉伸强度 [MPa]: 18.6
- 弯曲模量 [MPa]: 0.710
- 热变形温度 [℃]: 54.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | F50, Condition B; ASTM D-1693 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 0.710 GPa | 103 ksi | ASTM D790 |
| Impact Test | 237 J @Thickness 6.35 mm, Temperature -40.0 °C | 175 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | Impact Strength; Max Force; ARM |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 133 °C | 271 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.5 °C | 130 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |