- 熔体流动速率 [g/10min]: 0.34
- 密度 [g/cm3]: 0.946
- 缺口冲击强度: 4.27
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 5000 hour | >= 5000 hour | ASTM D1693 cond. B 100% lgepal |
| Melt Flow | 0.34 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.34 g/10 min @Load 11.0 lb, Temperature 374 °F | |
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 22.8 MPa | >= 3300 psi | ASTM D 638 type IV |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D 638, type IV |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.27 J/cm @Thickness 3.17 mm | 8.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 258 °F | ASTM D3417 |