- 密度 [g/cm3]: 0.954
- 缺口冲击强度: 6.67
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 200 hour | >= 200 hour | ASTM D1693 cond. B 10% lgepal |
| >= 1000 hour | >= 1000 hour | ASTM D1693 cond. B 100% lgepal | |
| High Load Melt Index | 5.5 g/10 min @Load 21.6 kg | 5.5 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | >= 39.3 MPa | >= 5700 psi | ASTM D 638 type IV |
| Tensile Strength, Yield | >= 28.3 MPa | >= 4100 psi | ASTM D 638 type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D 638, type IV |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D 790 |
| Izod Impact, Notched | 6.67 J/cm @Thickness 3.17 mm | 12.5 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 263 °F | ASTM D3417 |