- 密度 [g/cm3]: 0.949
- 缺口冲击强度: 6.41
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | >= 360 hour | >= 360 hour | ASTM D1693 cond. B 100% lgepal |
| Thermal Stress Crack Resistance | >= 250 hour | >= 250 hour | ASTM D 1693 |
| High Load Melt Index | 8.0 g/10 min @Load 21.6 kg | 8.0 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 260 °F | ASTM D3417 |