- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 22.1
- 弯曲模量 [MPa]: 0.965
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D 792 |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | ASTM D1693 cond. B 10% lgepal |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg | 0.55 g/10 min @Load 4.76 lb | ISO 1133 |
| 1.9 g/10 min @Load 5.00 kg | 1.9 g/10 min @Load 11.0 lb | ASTM D 1238 | |
| High Load Melt Index | 19 g/10 min @Load 21.6 kg | 19 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 41 | 41 | ASTM D 785 |
| Hardness, Shore D | 62 | 62 | ASTM D 2240 |
| Tensile Strength, Yield | >= 22.1 MPa | >= 3200 psi | ASTM D 638 type IV |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D 638, type IV |
| Flexural Modulus | 0.965 GPa | 140 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C | 10.0 µin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D 1525 |