- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.9495
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9495 g/cc | 0.03430 lb/in³ | ISO 1183 |
| Thermal Stress Crack Resistance | >= 250 hour | >= 250 hour | ASTM D 1693 |
| Melt Flow | 8.0 g/10 min @Temperature 190 °C | 8.0 g/10 min @Temperature 374 °F | High Load; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527 |
| Elongation at Yield | 11 % | 11 % | ISO 527 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 |