- 密度 [g/cm3]: 0.949
- 拉伸强度 [MPa]: 24.8
- 弯曲模量 [MPa]: 1.17
- 脆化温度 [℃]: -90.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 600 hour | >= 600 hour | Condition A (100% Igepal), F50; ASTM D1693 |
| >= 600 hour | >= 600 hour | Condition B (10% Igepal), F50; ASTM D1693 | |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | 2" (50mm) per min.; ASTM D638 Type IV |
| Elongation at Break | >= 600 % | >= 600 % | 2" (50mm) per min.; ASTM D638 Type IV |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -90.6 °C | <= -131 °F | ASTM D746 |