- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.966
- 缺口冲击强度: 4.9
- 拉伸强度 [MPa]: 31.4
- 弯曲强度 [MPa]: 34.3
- 弯曲模量 [MPa]: 1.08
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.966 g/cc | 0.0349 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 40 hour | 40 hour | ASTM D1693 |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.3 MPa | 4980 psi | ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.08 GPa | 156 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 134 °C | 273 °F | ASTM D2117 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |