- 熔体流动速率 [g/10min]: 0.12
- 密度 [g/cm3]: 0.956
- 拉伸强度 [MPa]: 22.0
- 弯曲强度 [MPa]: 34.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Melt Flow | 0.12 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.12 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 1600 % | 1600 % | ASTM D638 |