- 熔体流动速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.93
- 拉伸强度 [MPa]: 17.0
- 热变形温度 [℃]: 65.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.930 g/cc | 0.930 g/cc | ASTM D792 | ||
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 | ||
| Density of Compound | 0.930 g/cc | 0.0336 lb/in³ | Indicative density (PE only); ISO 1872-1 | ||
| Water Absorption | <= 0.0100 % | <= 0.0100 % | ISO 62 | ||
| Moisture Absorption | <= 0.0100 % | <= 0.0100 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Measurement | 2585 | 2585 | Intrinsic viscosity ml/g; ISO 1628-3 | ||
| Viscosity Test | 3050 cm³/g | 3050 cm³/g | ISO 307, 1157, 1628 | ||
| 3050 cm³/g | 3050 cm³/g | ISO 1628-3 | |||
| Melt Flow | <= 0.100 g/10 min @Load 21.6 kg, Temperature 190 °C | <= 0.100 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| <= 0.100 g/10 min @Load 21.6 kg, Temperature 190 °C | <= 0.100 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60.0 | 60.0 | 15 sec; ISO 868 | ||
| 62.0 | 62.0 | ASTM D2240 | |||
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | ISO 2039-1 | ||
| Tensile Stress | 0.380 MPa | 55.1 psi | Elongational Stress F (150/10); ISO 11542-2 | ||
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | 50mm/min; ISO 527-2/1A | ||
| 21.4 MPa | 3100 psi | ASTM D638 | |||
| Elongation at Break | >= 50.0 % | >= 50.0 % | 50mm/min; ISO 527-2/1A | ||
| >= 350 % @Temperature 22.8 °C | >= 350 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 20.0 % | 20.0 % | 50mm/min; ISO 527-2/1A | ||
| <= 20.0 % @Temperature 22.8 °C | <= 20.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 0.680 GPa | 98.6 ksi | 1mm/min; ISO 527-2/1A | ||
| 0.6998 GPa @Temperature 22.8 °C | 101.5 ksi @Temperature 73.0 °F | ASTM D638 | |||
| Izod Impact, Unnotched | NB | NB | ASTM D256 | ||
| Charpy Impact, Notched | 18.0 J/cm² | 85.7 ft-lb/in² | 14° V-notch both sides; ISO 11542-2 | ||
| Coefficient of Friction, Dynamic | 0.100 | 0.100 | steel; Internal | ||
| Tensile Creep Modulus, 1 hour | 430 MPa | 62400 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 230 MPa | 33400 psi | ISO 899-1 | ||
| K Factor (Wear Factor) | 90.0 | 90.0 | Wear by sandslurry method (based on GUR 4120=100); Internal | ||
| 90.0 | 90.0 | Abrasion loss; Internal | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | IEC 60093 | ||
| >= 1.00e+13 ohm | >= 1.00e+13 ohm | ASTM D257 | |||
| Dielectric Constant | 2.10 @Frequency 100 Hz | 2.10 @Frequency 100 Hz | IEC 60250 | ||
| 3.00 @Frequency 1.00e+6 Hz | 3.00 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 3.00 @Frequency 1.00e+6 Hz | 3.00 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.000390 @Frequency 100 Hz | 0.000390 @Frequency 100 Hz | IEC 60250 | ||
| 0.00100 @Frequency 1.00e+6 Hz | 0.00100 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 198 µm/m-°C | 110 µin/in-°F | ASTM D696 | ||
| 200 µm/m-°C | 111 µin/in-°F | ISO 11359-2 | |||
| Specific Heat Capacity | 1.84 J/g-°C | 0.440 BTU/lb-°F | Internal | ||
| 1.84 J/g-°C | 0.440 BTU/lb-°F | Internal | |||
| Thermal Conductivity | 0.410 W/m-K | 2.85 BTU-in/hr-ft²-°F | Internal | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C | 149 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 80.0 °C | 176 °F | B50 (50°C/h 50N); ISO 306 | ||
| 80.0 °C | 176 °F | ASTM D1525 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 | ||
| Descriptive Properties | |||||
| Comp. molding cooling rate | 15°K/min | ISO 293 | |||
| Comp. molding mold temperature °C | 210 | ISO 293 | |||
| Injection molding | No | ||||
| Other extrusion | Yes | ||||
| Powder | Yes | ||||
| pvT (Generic Grade reference) | PE-HMW, QED, 50 G0012 | ||||
| Special Information | For Ram Extrusion and Compression Molding only | ||||
| Transfer molding | Yes | ||||