- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.854
- 弯曲强度 [MPa]: 26.2
- 弯曲模量 [MPa]: 1.59
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.427 g/cc | 1.427 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Thickness 3.17 mm | 0.010 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 1.59 GPa | 230 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 26.9 MPa | 3900 psi | ASTM D790 |
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |