- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.621
- 热变形温度 [℃]: 70.0
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| ESCR 10% Igepal® | >= 120 hour | >= 120 hour | ARM Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | At 50 mm/min; ASTM D683 IV |
| Flexural Modulus | 0.621 GPa | 90.0 ksi | At 2 mm/min; ASTM D790 |
| Dart drop Total Energy | 210.0 J/cm | 0.3934 ft-lb/mil | (-4oF/-20°C); ASTM D3763 |
| Dart Drop | 152 g/micron | 3860 g/mil | Instrumented Falling Weight (-4°F/-20°C); ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |