- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.948
- 拉伸强度 [MPa]: 24.8
- 弯曲模量 [MPa]: 0.600
- 脆化温度 [℃]: -76.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.948 g/cc | 0.0342 lb/in³ | Compound; ASTM D792 |
ESCR 10% Igepal® | >= 2000 hour | >= 2000 hour | ASTM D1693/B |
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 55 | 55 | ASTM D2240 |
Tensile Strength, Yield | >= 24.8 MPa | >= 3600 psi | ASTM D638 |
Elongation at Break | >= 700 % | >= 700 % | ASTM D638 |
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Dielectric Strength | >= 39.4 kV/mm | >= 1000 kV/in | At 20 mils; ASTM D149 |
Thermal Properties | Metric | English | Comments |
Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |