- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ISO 1183 |
| Melt Flow | 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C | 1.0 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | At 50 mm/min; ISO/DIS 6259 |
| Tensile Strength, Yield | 20.0000 MPa | 2900.75 psi | At 50 mm/min; ISO/DIS 6259 |
| Elongation at Break | 180 % | 180 % | ISO/DIS 6259 |
| Elongation at Yield | 13 % | 13 % | ISO/DIS 6259 |
| Modulus of Elasticity | 0.630 GPa | 91.4 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 µm/m-°C @Temperature -20.0 °C | 50.0 µin/in-°F @Temperature -4.00 °F | ASTM D696 |
| 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 | |
| 500 µm/m-°C @Temperature 100 °C | 278 µin/in-°F @Temperature 212 °F | ASTM D696 | |
| Specific Heat Capacity | 2.10 J/g-°C | 0.502 BTU/lb-°F | |
| Thermal Conductivity | 0.410 W/m-K | 2.85 BTU-in/hr-ft²-°F | DIN 52612 |
| Vicat Softening Point | 122 °C | 252 °F | ISO 306 |