- 密度 [g/cm3]: 0.934
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | base resin; ISO 1872-2/ISO 1183 | ||
| 0.937 g/cc | 0.0339 lb/in³ | compound; ISO 1872-2/ISO 1183 | |||
| Thermal Stress Crack Resistance | 1.50 hour @Temperature 105 °C | 1.50 hour @Temperature 221 °F | IEC 60811-4-2/A | ||
| Oxidative Induction Time (OIT) | 50 min @Temperature 200 °C | 50 min @Temperature 392 °F | IEC 60811-4-2/B | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 11.0 MPa | 1600 psi | 50mm/min; ISO 527 | ||
| 11.0 MPa | 1600 psi | 50mm/min, expanded 35% insulation; IEC 60811-1-1 | |||
| Elongation at Break | 500 % | 500 % | 50mm/min; ISO 527 | ||
| 500 % | 500 % | 50mm/min, 35% expanded insulation; IEC 60811-1-1 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.31 @Frequency 1.00e+6 Hz | 2.31 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.00050 @Frequency 1.00e+6 Hz | 0.00050 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 100 - 120 °C | 212 - 248 °F | conductor preheating temperature | ||
| Zone 1 | 155 °C | 311 °F | |||
| Zone 2 | 170 °C | 338 °F | |||
| Zone 3 | 185 °C | 365 °F | |||
| Zone 4 | 195 °C | 383 °F | |||
| Die Temperature | 195 °C | 383 °F | |||
| Melt Temperature | 195 - 200 °C | 383 - 392 °F | |||
| Descriptive Properties | |||||
| Petroleum Jelly Absorption (%) | 10 | IEC 60811-4-2 | |||