- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg, Temperature 190 °C | 20 g/10 min @Load 47.6 lb, Temperature 374 °F | HLMI; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 21.4 MPa | 3100 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 21.4 MPa | 3100 psi | ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 1.97 g/micron | 50.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.7 g/micron | 500 g/mil | ASTM D1922 |
| Dart Drop | 5.12 g/micron | 130 g/mil | 26 in (66 cm); ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.1 MPa | 6100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 42.1 MPa | 6100 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 °C | 421 °F | |
| Die Opening | 0.0890 cm | 0.0350 in | |