- 密度 [g/cm3]: 0.943
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.720
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in³ | ASTM D1505 | ||
| Melt Index of Compound | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 63 | 63 | ASTM D2240 | ||
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 1000 % | 1000 % | 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 0.720 GPa | 104 ksi | 1.3 mm/min; ASTM D790 | ||
| Impact | 19 @Temperature -20.0 °C | 19 @Temperature -4.00 °F | J/mm, instrumented impact, rotomolded test sample; ICO R&D1.14 | ||
| Descriptive Properties | |||||
| UV Light Weatherometer Test | 8000 hours | ASTM G26 | |||