- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.941
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.760
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | |
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 37.0 cm | 14.6 in | NOVA |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 16 % | 16 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 0.760 GPa | 110 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |