- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.9385
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9385 g/cc | 0.03391 lb/in³ | ASTM D1505 | ||
| ESCR 100% Igepal® | >= 2000 hour | >= 2000 hour | F50; ASTM D1693-B | ||
| Oxidative Induction Time (OIT) | >= 100 min | >= 100 min | At 200°C with oxygen in aluminum pan.; ASTM D3895 | ||
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | I2; ASTM D1238 | ||
| 20 g/10 min | 20 g/10 min | I21; ASTM D238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 | ||
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 | ||
| Elongation at Break | >= 850 % | >= 850 % | ASTM D638 | ||
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ASTM D790 | ||
| Descriptive Properties | |||||
| Process | Sheet Extrusion | ||||