Total MDPE HF 513 Medium Density Polyethylene, Blown Film

Total MDPE HF 513 Medium Density Polyethylene, Blown Film 物性表: Total MDPE HF 513 Medium Density Polyethylene, Blown Film物性表及特性介绍,Total MDPE HF 513 Medium Density Polyethylene, Blown Film注塑参数详情,如需Total MDPE HF 513 Medium Density Polyethylene, Blown Film下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.15
  • 弯曲模量 [MPa]: 0.620
 
Physical PropertiesMetricEnglishComments
Specific Gravity 0.934 g/cc0.934 g/ccISO 1183
Melt Flow  0.15 g/10 min
@Load 2.16 kg,
Temperature 190 °C
0.15 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ISO 1133
 14.5 g/10 min
@Load 213.6 kg,
Temperature 190 °C
14.5 g/10 min
@Load 470.9 lb,
Temperature 374 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD  18.0 MPa
@Thickness 0.0400 mm
2610 psi
@Thickness 0.00157 in
ISO 527-3
 20.0 MPa
@Thickness 0.0200 mm
2900 psi
@Thickness 0.000787 in
ISO 527-3
Film Tensile Strength at Yield, TD  18.0 MPa
@Thickness 0.0400 mm
2610 psi
@Thickness 0.00157 in
ISO 527-3
 19.0 MPa
@Thickness 0.0200 mm
2760 psi
@Thickness 0.000787 in
ISO 527-3
Film Elongation at Break, MD  400 %
@Thickness 0.0200 mm
400 %
@Thickness 0.000787 in
ISO 527-3
 540 %
@Thickness 0.0400 mm
540 %
@Thickness 0.00157 in
ISO 527-3
Film Elongation at Break, TD  500 %
@Thickness 0.0200 mm
500 %
@Thickness 0.000787 in
ISO 527-3
 620 %
@Thickness 0.0400 mm
620 %
@Thickness 0.00157 in
ISO 527-3
Flexural Modulus 0.620 GPa
@Strain <=0.250 %
89.9 ksi
@Strain <=0.250 %
ISO 178
Elmendorf Tear Strength, MD  1.10 g/micron
@Thickness 0.0200 mm
27.9 g/mil
@Thickness 0.000787 in
ISO 6383-1
 2.40 g/micron
@Thickness 0.0400 mm
61.0 g/mil
@Thickness 0.00157 in
ISO 6383-1
Elmendorf Tear Strength, TD  13.8 g/micron
@Thickness 0.0200 mm
351 g/mil
@Thickness 0.000787 in
ISO 6383-1
 18.9 g/micron
@Thickness 0.0400 mm
480 g/mil
@Thickness 0.00157 in
ISO 6383-1
Dart drop Test  220 g
@Thickness 0.0200 mm
0.485 lb
@Thickness 0.000787 in
ISO 7765-1
 290 g
@Thickness 0.0400 mm
0.639 lb
@Thickness 0.00157 in
ISO 7765-1
Film Tensile Strength at Break, MD  55.0 MPa
@Thickness 0.0400 mm
7980 psi
@Thickness 0.00157 in
ISO 527-3
 65.0 MPa
@Thickness 0.0200 mm
9430 psi
@Thickness 0.000787 in
ISO 527-3
Film Tensile Strength at Break, TD  52.0 MPa
@Thickness 0.0200 mm
7540 psi
@Thickness 0.000787 in
ISO 527-3
 52.0 MPa
@Thickness 0.0400 mm
7540 psi
@Thickness 0.00157 in
ISO 527-3
 
Thermal PropertiesMetricEnglishComments
Melting Point 125 °C257 °FISO 11357
Vicat Softening Point 118 °C244 °FISO 306
 
Processing PropertiesMetricEnglishComments
Processing Temperature 190 - 220 °C374 - 428 °FExtrusion

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-42996.html

免责声明: 本文 Total MDPE HF 513 Medium Density Polyethylene, Blown Film 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4