- 密度 [g/cm3]: 0.929
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 20.0
- 热变形温度 [℃]: 61.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 14 % | 14 % | |
| Tensile Modulus | 0.725 GPa | 105 ksi | |
| Tensile Creep Modulus, 1 hour | 260 MPa | 37700 psi | |
| Tensile Creep Modulus, 1000 hours | 200 MPa | 29000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 210 µm/m-°C @Temperature 20.0 °C | 117 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 136 °C | 277 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 61.0 °C | 142 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | |
| Vicat Softening Point | 81.0 °C | 178 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm | HB @Thickness 0.0157 in | |