| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Permeability | 0.030 | 0.030 | [g / hr / ft2 / in. Hg] at 73°F and 50% RH; ASTM D96-93 |
| Thickness | 38.1 microns | 1.50 mil | adhesive thickness; ASTM D3652 |
| 50.8 microns | 2.00 mil | backing thickness; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 0.138 MPa | 20.0 psi | ASTM D3759 |
| Elongation at Break | 120 % | 120 % | ASTM D3759 |
| Adhesive Bond Strength | 11.7 MPa | 1700 psi | initial adhesion to steel; ASTM D3330 |
| 17.2 MPa | 2500 psi | adhesion to steel after 3 days at 72°F; ASTM D3330 | |
| 17.2 MPa | 2500 psi | initial adhesion to Saran™ film; ASTM D3330 | |
| 18.6 MPa | 2700 psi | adhesion to Saran™ film after 3 days at 72°F; ASTM D3330 | |
| Thermal Properties | Metric | English | Comments |
| Flammability Test | 0.00 | 0.00 | Flame Spread; ASTM E84-98 |
| Smoke Density | 15 min | 15 min | ASTM E84-98 |