SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE)

SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) 物性表: SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE)物性表及特性介绍,SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE)注塑参数详情,如需SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.84
  • 缺口冲击强度: 5.51
  • 拉伸强度 [MPa]: 52.0
  • 弯曲模量 [MPa]: 3.78
  • 热变形温度 [℃]: 219.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.85 g/cc1.85 g/ccASTM D792
Density 1.84 g/cc0.0665 lb/in³ASTM D792
Moisture Absorption 0.0100 %0.0100 %23°C / 50% RH; ISO 62
 0.0200 %0.0200 %50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow >= 0.020 cm/cm
@Time 86400 sec
>= 0.020 in/in
@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm
@Time 86400 sec
0.020 - 0.040 in/in
@Time 24.0 hour
ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 49.0 MPa7110 psiType I, 5 mm/min; ASTM D638
 51.0 MPa7400 psi5 mm/min; ISO 527
Tensile Strength, Yield 52.0 MPa7540 psi5 mm/min; ISO 527
 54.0 MPa7830 psiType I, 5 mm/min; ASTM D638
Elongation at Break 9.8 %9.8 %5 mm/min; ISO 527
 10.7 %10.7 %Type I, 5 mm/min; ASTM D638
Elongation at Yield 9.1 %9.1 %5 mm/min; ISO 527
 9.4 %9.4 %Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.40 GPa638 ksi1 mm/min; ISO 527
 4.86 GPa705 ksi5 mm/min; ASTM D638
Flexural Strength 72.0 MPa10400 psiISO 178
Flexural Modulus 3.78 GPa548 ksi2 mm/min; ISO 178
 4.02 GPa583 ksi1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.51 J/cm10.3 ft-lb/inASTM D256
Izod Impact, Unnotched 14.6 J/cm27.4 ft-lb/inASTM D4812
Izod Impact, Notched (ISO) 45.0 kJ/m²21.4 ft-lb/in²80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 96.0 kJ/m²45.7 ft-lb/in²80*10*4; ISO 180/1U
Dart Drop, Total Energy 21.0 J
@Temperature 23.0 °C
15.5 ft-lb
@Temperature 73.4 °F
ASTM D3763
Impact Test 10.0 J7.38 ft-lbMultiaxial Impact; ISO 6603
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 59.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
32.8 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 76.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
42.2 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 219 °C426 °FFlatw 80*10*4 sp=64mm; ISO 75/Bf
 240 °C
@Thickness 3.20 mm
464 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 112 °C234 °FFlatw 80*10*4 sp=64mm; ISO 75/Af
 132 °C
@Thickness 3.20 mm
270 °F
@Thickness 0.126 in
unannealed; ASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-43217.html

免责声明: 本文 SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4