- 密度 [g/cm3]: 1.73
- 缺口冲击强度: 3.52
- 弯曲模量 [MPa]: 11.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D 638 |
| 90.0 MPa | 13100 psi | ASTM D 638 | |
| Elongation at Break | 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D 638 |
| 4.9 % | 4.9 % | ASTM D 638 | |
| Tensile Modulus | 11.71 GPa | 1698 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 137 MPa | 19900 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| 137 MPa | 19900 psi | ASTM D 790 | |
| Flexural Modulus | 11.03 GPa | 1600 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 11.03 GPa | 1600 ksi | ASTM D 790 | |
| Izod Impact, Notched | 3.52 J/cm @Temperature 23.0 °C | 6.59 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 12.38 J/cm @Temperature 23.0 °C | 23.19 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D 648 |