- 密度 [g/cm3]: 1.74
- 缺口冲击强度: 1.81
- 弯曲模量 [MPa]: 10.54
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm @Time 86400 sec | 0.0065 in/in @Time 24.0 hour | ISO 294 |
| 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm @Time 86400 sec | 0.022 in/in @Time 24.0 hour | ASTM D955 |
| 0.0222 cm/cm @Time 86400 sec | 0.0222 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ISO 527 |
| 60.0 MPa | 8700 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.5 % | 2.5 % | ASTM D638 | |
| Tensile Modulus | 12.18 GPa | 1767 ksi | 1 mm/min; ISO 527 |
| 13.3 GPa | 1930 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 106 MPa | 15400 psi | ASTM D790 |
| 120 MPa | 17400 psi | ISO 178 | |
| Flexural Modulus | 10.54 GPa | 1529 ksi | ASTM D790 |
| 10.55 GPa | 1530 ksi | ISO 178 | |
| Izod Impact, Notched | 1.81 J/cm | 3.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 14.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 25.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 14.2 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 30.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 30.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 252 °C @Thickness 3.20 mm | 486 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm | 406 °F @Thickness 0.126 in | unannealed; ASTM D648 | |