- 密度 [g/cm3]: 1.68
- 拉伸强度 [MPa]: 29.6
- 断裂伸长率 [%]: 26.2
- 弯曲模量 [MPa]: 1.69
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.10 % | <= 0.10 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Tensile Modulus | 1.65 GPa | 240 ksi | ASTM D638 |
| Flexural Yield Strength | 26.2 MPa | 3800 psi | ASTM D790 |
| Flexural Modulus | 1.69 GPa | 245 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.5 @Frequency 1000 Hz | 2.5 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 101 µm/m-°C @Temperature 20.0 °C | 56.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 241 °C | 465 °F | ASTM D4591 |
| Maximum Service Temperature, Air | 149 °C | 300 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 56 % | 56 % | ASTM D2863 |